C12200 Copper Alloy
Available Forms: Tubes, Pipes, Sheets, Plates, Coils, Strips
Size Range: Custom sizes available (Tubes: 1/4" to 12" diameter, Sheets: 0.1mm to 25mm thickness)
Temper: O60 (Soft), H00 (Light Drawn), H01 (¼ Hard), H02 (½ Hard), H03 (¾ Hard), H04 (Full Hard)
Surface Finish: Mill finish, polished, cleaned, or as specified
C12200 copper is a phosphorus-deoxidized non-arsenical copper containing 0.015-0.040% phosphorus, which acts as a deoxidizing agent during melting and processing. This results in a material free from oxygen-related defects, making C12200 copper alloy particularly suitable for applications involving welding, brazing, and exposure to hydrogen atmospheres. Our C12200 products are manufactured under stringent quality control measures and are available in tubes, pipes, sheets, and plates that meet or exceed international standards for purity and performance.
Specifications
|
Property |
Value/Description |
|
UNS Designation |
C12200 |
|
Common Names |
DHP Copper, Phosphorus Deoxidized Copper |
|
Standards |
ASTM B42, ASTM B68, ASTM B75, ASTM B88, ASTM B152, ASTM B587 |
|
Available Forms |
Tubes, Pipes, Sheets, Plates, Coils, Strips |
|
Size Range |
Custom sizes available (Tubes: 1/4" to 12" diameter, Sheets: 0.1mm to 25mm thickness) |
|
Temper |
O60 (Soft), H00 (Light Drawn), H01 (¼ Hard), H02 (½ Hard), H03 (¾ Hard), H04 (Full Hard) |
|
Surface Finish |
Mill finish, polished, cleaned, or as specified |
Chemical Composition
|
Element |
Content (%) |
|
Copper (Cu) |
≥ 99.90 |
|
Phosphorus (P) |
0.015 - 0.040 |
|
Oxygen (O) |
≤ 0.01 |
|
Other Impurities |
≤ 0.05 (total) |
Mechanical Properties
|
Property |
Annealed (O60) |
½ Hard (H02) |
Hard (H04) |
|
Tensile Strength |
32 ksi (220 MPa) |
38 ksi (262 MPa) |
42 ksi (290 MPa) |
|
Yield Strength (0.5% Ext) |
10 ksi (69 MPa) |
30 ksi (207 MPa) |
36 ksi (248 MPa) |
|
Elongation (% in 2") |
45% |
15% |
8% |
|
Hardness (Rockwell F) |
40 HRF |
65 HRF |
80 HRF |
|
Electrical Conductivity |
92% IACS |
90% IACS |
88% IACS |
|
Thermal Conductivity |
222 W/m·K |
218 W/m·K |
215 W/m·K |
Performance Characteristics
Weldability
Excellent (all conventional methods)
Brazing Characteristics
Superior
Corrosion Resistance
Excellent in water and steam
Formability
Excellent - both hot and cold working
Annealing Temperature
700-1200°F (371-649°C)
Stress Relief Temperature
400-600°F (204-316°C)
Global Project Experience
Our C12200 copper alloy has been specified in:
Commercial HVAC systems
Residential and commercial plumbing installations
Industrial refrigeration plants
Power generation facilities
Chemical processing equipment
90% client retention rate with consistent repeat orders from HVACR and plumbing manufacturers.
Request Quote Today
Contact our technical sales team today for immediate assistance with your C12200 copper alloy requirements. Let us provide the quality and service excellence that keeps industry leaders coming back!