6061 Aluminum Plate
Thickness: 0.5mm - 150mm (0.02" - 6")
Width: 500mm - 2500mm (20" - 98")
Length: 1000mm - 12000mm (39" - 472")
Temper Conditions: O, T4, T6, T651, T652
Surface Finish: Mill Finish, Anodized, Powder Coated, Brushed
Certification: ISO 9001, SGS test report, material certificate (MTC)
BAOHUI STEEL supplies 6061 Aluminum Plate, a premium heat-treatable aluminum alloy containing magnesium and silicon as its primary alloying elements. In the T6 temper, this alloy offers a superior combination of high strength, excellent corrosion resistance, and good machining characteristics. Our 6061 aluminum plates are widely used in structural components, automotive parts, and various industrial applications where strength and weight ratio are critical.
Key Features
High Strength-to-Weight Ratio
Strong yet lightweight structural solution
Excellent Corrosion Resistance
Good resistance to atmospheric and marine environments
Good Machinability
Can be easily machined to precise tolerances
Excellent Weldability
All common welding methods can be employed
Heat Treatable
Can be solution heat-treated and aged to enhance properties
Anodizing Response
Excellent for surface treatment and coloring
Product Specifications
|
Parameter |
Specification Range |
|
Thickness |
0.5mm - 150mm (0.02" - 6") |
|
Width |
500mm - 2500mm (20" - 98") |
|
Length |
1000mm - 12000mm (39" - 472") |
|
Temper Conditions |
O, T4, T6, T651, T652 |
|
Surface Finish |
Mill Finish, Anodized, Powder Coated, Brushed |
|
Applicable Standards |
ASTM B209, AMS 4027, AMS 4028, EN AW-6061 |
Chemical Composition
|
Element |
Content (%) |
|
Aluminum (Al) |
95.8 - 98.6 |
|
Magnesium (Mg) |
0.8 - 1.2 |
|
Silicon (Si) |
0.4 - 0.8 |
|
Iron (Fe) |
≤ 0.7 |
|
Copper (Cu) |
0.15 - 0.40 |
|
Chromium (Cr) |
0.04 - 0.35 |
|
Zinc (Zn) |
≤ 0.25 |
|
Manganese (Mn) |
≤ 0.15 |
|
Titanium (Ti) |
≤ 0.15 |
Mechanical Properties
|
Temper |
Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation (%) |
Hardness (Brinell) |
|
O (Annealed) |
125 |
55 |
25 |
30 |
|
T4 (Solution Heat Treated) |
240 |
145 |
22 |
65 |
|
T6 (Solution & Artificial Aged) |
310 |
275 |
12 |
95 |
|
T651 (Stress Relieved) |
310 |
275 |
12 |
95 |
Physical Properties
|
Property |
Value |
|
Density |
2.70 g/cm³ (0.098 lb/in³) |
|
Melting Point |
582 - 652°C (1080 - 1205°F) |
|
Electrical Conductivity |
43% IACS |
|
Thermal Conductivity |
167 W/m·K (1160 BTU·in/hr·ft²·°F) |
|
Thermal Expansion Coefficient |
23.6 × 10⁻⁶/°C (13.1 × 10⁻⁶/°F) |
Quality Commitment of 6061 aluminum plate
EN 10204 3.1 Certification
Full Chemical & Mechanical Testing
Dimensional Accuracy Guarantee
Third-Party Inspection Support
FAQ
Q: What is the difference between 6061-T6 and 6061-T651?
A: T651 indicates the plate has been stress-relieved by stretching after heat treatment, providing better stability for machining.
Q: Can 6061 aluminum be welded?
A: Yes, it has excellent weldability using TIG, MIG, and other common methods.
Q: What is the maximum service temperature?
A: Not recommended for prolonged use above 175°C due to strength reduction.
Q: Is 6061 suitable for marine applications?
A: Yes, it offers good corrosion resistance in marine environments.
Q: What is your standard lead time?
A: 7-15 days for standard sizes, 15-25 days for custom processing.
Request Pricing & Technical Information
Contact Our6061 aluminum plate Experts Today!
Hot Tags: 6061 aluminum plate, China 6061 aluminum plate manufacturers, suppliers, factory, 1060 aluminum sheet, 5083 Aluminum Alloy, 5454 Aluminum Alloy, Aluminium 7075 T6, Aluminum Sheet and Plate EN AW 5754 H22, UNS A96063
Previous
5083 Aluminum AlloyYou Might Also Like
Send Inquiry